In situ optical sub-wavelength thickness control of porous anodic aluminum oxide

• Aleksandrs Dutovs,
• Raimonds Popļausks,
• Oskars Putāns,
• Vladislavs Perkanuks,
• Aušrinė Jurkevičiūtė,
• Tomas Tamulevičius,
• Uldis Malinovskis,
• Iryna Olyshevets,
• Donats Erts and
• Juris Prikulis

Beilstein J. Nanotechnol. 2024, 15, 126–133, doi:10.3762/bjnano.15.12

• , Latvia Faculty of Physics, Mathematics and Optometry, University of Latvia, 3 Jelgavas Str., Riga LV-1004, Latvia 10.3762/bjnano.15.12 Abstract Porous anodic aluminum oxide (PAAO), sometimes referred to as nanoporous anodic alumina, serves as a cost-effective template for nanofabrication in many fields

• microscopy and is particularly valuable for the small-scale production of PAAO-based functional optical coatings. Keywords: electrochemistry; ellipsometry; porous anodic alumina; spectroscopy; thin films; Introduction Porous anodic aluminum oxide (PAAO) is a versatile self-organized material with

Uniform arrays of gold nanoelectrodes with tuneable recess depth

• Elena O. Gordeeva,
• Ilya V. Roslyakov,
• Alexey P. Leontiev,
• Alexey A. Klimenko and
• Kirill S. Napolskii

Beilstein J. Nanotechnol. 2021, 12, 957–964, doi:10.3762/bjnano.12.72

• approaches for the preparation of such systems is templated electrodeposition. In the present study, porous anodic alumina templates are used to prepare Au nanoelectrode arrays. Multistage electrodeposition is proposed for the formation of recessed electrodes with the ability to tune the distance between the

• pathways to further improve the recessed nanoelectrode arrays based on anodic alumina templates are discussed. Keywords: anodic alumina; gold; nanoelectrode array; recessed electrode; templated electrodeposition; Introduction A nanoelectrode array (NEA) is a set of regularly arranged isolated metal

• of Cu/Au/Cu segments into the pores of an anodic alumina template with the subsequent selective dissolution of the sputtered Cu current collector and the first Cu segment. The reported design of NEAs allows one to tune the recess of Au nanoelectrodes relative to the AAO surface with high precision

A 3D-polyphenylalanine network inside porous alumina: Synthesis and characterization of an inorganic–organic composite membrane

• Jonathan Stott and
• Jörg J. Schneider

Beilstein J. Nanotechnol. 2020, 11, 938–951, doi:10.3762/bjnano.11.78

• oligomerization [19][20][21]. Films of poly(γ-benzyl-ʟ-glutamate) were surface-grafted within nanoporous anodic alumina (AAO) by surface-initiated polymerization of poly(γ-benzyl-ʟ-glutamate)-NCA [22][23]. Three-dimensional fibrillar networks consisting of supramolecular assemblies of oligomers or polypeptides

Ultrathin hydrophobic films based on the metal organic framework UiO-66-COOH(Zr)

• Miguel A. Andrés,
• Clemence Sicard,
• Christian Serre,
• Olivier Roubeau and
• Ignacio Gascón

Beilstein J. Nanotechnol. 2019, 10, 654–665, doi:10.3762/bjnano.10.65

• important characteristic in many practical applications. Aguado et al. [37] obtained hydrophobic SIM-2 by post-synthetic functionalization of SIM-1 films deposited onto anodic alumina disks (MOF layer thickness ≈20 µm). Grzybowski et al. [45] obtained freestanding, porphyrin-based MOF films approximately

Nanoporous water oxidation electrodes with a low loading of laser-deposited Ru/C exhibit enhanced corrosion stability

• Sandra Haschke,
• Dmitrii Pankin,
• Vladimir Mikhailovskii,
• Maïssa K. S. Barr,
• Adriana Both-Engel,
• Alina Manshina and
• Julien Bachmann

Beilstein J. Nanotechnol. 2019, 10, 157–167, doi:10.3762/bjnano.10.15

• composite onto a novel nanoporous electrode surface with low noble metal loading and improved stability. The Ru/C is coated on the pore walls of anodic alumina templates in a one-step laser-induced deposition method from Ru3(CO)12 solutions. Scanning electron microscopy proves the presence of a continuous

• successful deposition method to the functionalization of highly ordered nanostructured anodic alumina templates [35][36][37][38][39] (Note: as our system is based on pores of diameter >50 nm, it is macroporous according to the IUPAC definition; we will use the more general wording “nanoporous” and

• procedure and renders it widely available. Laser-induced deposition on nanoporous substrates This successful Ru/C laser deposition can now be transferred to anodic alumina templates featuring ordered arrays of parallel and cylindrical nanopores. The full preparation procedure is delineated in Figure 5. In

Magnetism and magnetoresistance of single Ni–Cu alloy nanowires

• Andreea Costas,
• Camelia Florica,
• Elena Matei,
• Maria Eugenia Toimil-Molares,
• Ionel Stavarache,
• Andrei Kuncser,
• Victor Kuncser and
• Ionut Enculescu

Beilstein J. Nanotechnol. 2018, 9, 2345–2355, doi:10.3762/bjnano.9.219

• . Consequently, the magnetic properties of such nanowires can be tuned in agreement with the foreseen applications. The templates used are usually nanoporous ion-track polycarbonate membranes [21] and anodic alumina membranes [22]. Both Ni–Cu alloys and Ni–Cu multilayers have been intensively studied as simple

Magnetic properties of Fe₃O₄ antidot arrays synthesized by AFIR: atomic layer deposition, focused ion beam and thermal reduction

• Juan L. Palma,
• Alejandro Pereira,
• Raquel Álvaro,
• José Miguel García-Martín and
• Juan Escrig

Beilstein J. Nanotechnol. 2018, 9, 1728–1734, doi:10.3762/bjnano.9.164

• [23] and colloidal [24] lithography, porous anodic alumina [25][26], block copolymer templates [27], nanochannel glass [28] and focused ion beam (FIB) patterning [29][30]. Recently, we have proposed the fabrication of disordered antidot arrays through the thermal reduction of thin films synthesized by

Preparation and morphology-dependent wettability of porous alumina membranes

• Dmitry L. Shimanovich,
• Alla I. Vorobjova,
• Daria I. Tishkevich,
• Alex V. Trukhanov,
• Maxim V. Zdorovets and
• Artem L. Kozlovskiy

Beilstein J. Nanotechnol. 2018, 9, 1423–1436, doi:10.3762/bjnano.9.135

• alumina; wettability; Introduction Porous anodic alumina (PAA) is increasingly attracting the attention of scientists due to its unique ordered honeycomb cell structure. Such a structure allows the formation of many new micro- and nanoelements via a template-assistant method [1][2][3]. In addition, PAA

• altered from the Wenzel to the Cassie state. The main aim of this study is preparation and investigation of the wetting properties of porous membranes with an ordered structure based on anodic alumina (PAMs) with different pore lengths and diameters. For this purpose we carry out a comparative analysis of

• it is possible to develop a template that is suitable for various membrane technologies. Experimental In this study, various membranes were fabricated based on porous anodic alumina, prepared via a two-step anodization of Al foil using three distinct sets of conditions: type I – in an aqueous

Liquid permeation and chemical stability of anodic alumina membranes

• Dmitrii I. Petukhov,
• Dmitrii A. Buldakov,
• Alexey A. Tishkin,
• Alexey V. Lukashin and
• Andrei A. Eliseev

Beilstein J. Nanotechnol. 2017, 8, 561–570, doi:10.3762/bjnano.8.60

• , Russia 10.3762/bjnano.8.60 Abstract A study on the chemical stability of anodic alumina membranes and their performance in long-term water and organic solvent permeation experiments is reported. Anodic alumina possesses high stability for both protonic and aprotonic organic solvents. However, serious

• channels blocking. This process intensifies in basic pH due to the high positive charge of the anodic alumina surface. An approach for improving anodic aluminum oxide stability towards dissolution in water by carbon CVD coating of the membrane walls is suggested. Keywords: anodic alumina; carbon-modified

• media [1][13][14][15]. In contrast, the narrow pore size distribution of anodic alumina membranes should result in a sharp cut-off curve and excellent filtration characteristics [1]. The possible reason for low publishing and application activity in the field is the degradation of AAO membrane materials

Nanomechanical humidity detection through porous alumina cantilevers

• Olga Boytsova,
• Alexey Klimenko,
• Vasiliy Lebedev,
• Alexey Lukashin and
• Andrey Eliseev

Beilstein J. Nanotechnol. 2015, 6, 1332–1337, doi:10.3762/bjnano.6.137

• behavior of the resonance frequency of porous anodic alumina cantilever arrays during water vapor adsorption and emphasize their possible use in the micromechanical sensing of humidity levels at least in the range of 10–22%. The sensitivity of porous anodic aluminium oxide cantilevers (Δf/Δm) and the

• humidity sensitivity equal about 56 Hz/pg and about 100 Hz/%, respectively. The approach presented here for the design of anodic alumina cantilever arrays by the combination of anodic oxidation and photolithography enables easy control over porosity, surface area, geometric and mechanical characteristics

• present work we concentrated on the elaboration of experimental methods for the fabrication of anodic alumina cantilever arrays and their testing for adsorption of water vapors. Results and Discussion The proposed procedure for the fabrication of cantilever arrays combines anodic oxidation of aluminium

Electrical properties of single CdTe nanowires

• Elena Matei,
• Camelia Florica,
• Andreea Costas,
• María Eugenia Toimil-Molares and
• Ionut Enculescu

Beilstein J. Nanotechnol. 2015, 6, 444–450, doi:10.3762/bjnano.6.45

• excellent reproducibility and a narrow distribution of the geometrical characteristics [8][9][10][11][12][13]. The method typically makes use of a nanoporous membrane as a template along with a method for filling its pores. As templates, most used are polymer ion track membranes, anodic alumina and diblock

Self-organization of mesoscopic silver wires by electrochemical deposition

• Sheng Zhong,
• Thomas Koch,
• Stefan Walheim,
• Harald Rösner,
• Eberhard Nold,
• Aaron Kobler,
• Torsten Scherer,
• Di Wang,
• Christian Kübel,
• Mu Wang,
• Horst Hahn and
• Thomas Schimmel

Beilstein J. Nanotechnol. 2014, 5, 1285–1290, doi:10.3762/bjnano.5.142

• methods to fabricate mesoscale metallic wires: Electron beam lithography is a precise and well-controlled method, yet for larger numbers of wires rather expensive and time consuming. Electrochemically oxidized anodic alumina membrane (AAM) templates are also often used to fabricate metallic nanowires [24

3D-nanoarchitectured Pd/Ni catalysts prepared by atomic layer deposition for the electrooxidation of formic acid

• Loïc Assaud,
• Evans Monyoncho,
• Kristina Pitzschel,
• Anis Allagui,
• Matthieu Petit,
• Margrit Hanbücken,
• Elena A. Baranova and
• Lionel Santinacci

Beilstein J. Nanotechnol. 2014, 5, 162–172, doi:10.3762/bjnano.5.16

• the potential region from −0.75 to 0.4 V vs MSE at a scanning rate of 15 mV·s−1. The current densities have been reported per unit mass of Pd (details on the Pd mass calculations can be found in Supporting Information File 1). Schematic description of the anodic alumina template fabrication and

• , which were obtained with 40 to 145 Pd ALD cycles. The mass of Pd was estimated from the QCM measurements. SEM micrograph of an anodic alumina oxide template. After the electropolishing, a sacrificial film was firstly grown by applying 40 V in 0.3 M H2C2O4 for 24 h at T = 8 °C and then dissolved in

Preparation of electrochemically active silicon nanotubes in highly ordered arrays

• Tobias Grünzel,
• Young Joo Lee,
• Karsten Kuepper and
• Julien Bachmann

Beilstein J. Nanotechnol. 2013, 4, 655–664, doi:10.3762/bjnano.4.73

• pore walls of an anodic alumina template, followed by a thermal reduction with lithium vapor. This thermal reduction is quantitative, homogeneous over macroscopic samples, and it yields amorphous silicon and lithium oxide, at the exclusion of any lithium silicides. The reaction is characterized by

Macromolecular shape and interactions in layer-by-layer assemblies within cylindrical nanopores

• Thomas D. Lazzara,
• K. H. Aaron Lau,
• Wolfgang Knoll,
• Andreas Janshoff and
• Claudia Steinem

Beilstein J. Nanotechnol. 2012, 3, 475–484, doi:10.3762/bjnano.3.54

• elsewhere [22][51][52]: and are, respectively, the dielectric constant components normal and parallel to the AAO membrane surface; fpore is the pore volume fraction within the AAO, εalumina = 2.68 is the dielectric constant of bulk anodic alumina at λ = 632.8 nm, and εpore is the (effective) dielectric